UHMWPE Thread
UHMWPE THREAD
Material : UHMWPE Fiber/100% UHMWPE
Tenacity : >33 g/d
Density : 0.97g/cm3
Fineness : 20D-4800D
Color : White/Black/Grey/Blue/Red/Green/Army Green
Application : Mooring Rope/Cut Resistance Gloves/High Strength Fishing Line/Cut Resistance Fabric
Material : UHMWPE Fiber/100% UHMWPE
Tenacity : >28 g/d
Density : 0.97g/cm3
Fineness : 20D-4800D
Color : White/Black/Grey/Blue/Red/Green/Army Green
Application : Mooring Rope/Cut Resistance Gloves/High Strength Fishing Line/Cut Resistance Fabric
Available
Unavailable
Definition
Ultra high molecular weight polyethylene (UHMWPE) fiber yarn with it’s density of 0,97g/cm³, a modulus of 1150 cN/dtex and a tensile strength of 32 cN/dtex is a perfect yarn for high end applications.
The UHMWPE fiber (Ultra High Molecular Weight Polyethylene Yarn) has 15 times stronger than steel and 40% stronger than aramid when weight for weight basis. It is the strongest yarn today for making cut-resistance gloves, high-strength ropes, and bulletproof fabrics. Its tenacity at breaking up to 45g/D and has goods performance on anti-UV, anti-chemicals, and anti-cut.
Product Features
- BULLET-PROOF
- Anti-Impact
- Light Weight
- Anti-UV
- Corrosion-Resistant
- Dimensional Stability
- Radiation-Resistant
Abrasion-Resistant
Typical Technical Properties
- After 1500 Sunshine hours, its remaining strength is more than 80%.
- After 6 months in most chemicals (seawater, gas, etc.), its remaining strength is 100%.
- The UHMWPE ropes remaining strength is 100% after 1000 times loaded relative test.
- Melting Point is around 135-145, Highly resistant to abrasion, cutting, tearing
- Its relative times until break of Abrasion proof are more than 110 to 103.
- Its relative times until break of Winding proof are more than 110 to 103.
- Its strength of annulation is 12 up to 18g/d. its 10 up to 15g/d for collusion.
Color is bright white and poor for dyeing.
Data Table
| Specification | Tenacity | Modulus | Filament | Monofilament | Elongation | ||
| Denier | Dtex | (cN/dtex) (≥) | （g/d）(≥) | （cN/dtex)（≥） | tow | denier | % (≤） |
| 20D | 22 | 40 | 45 | 1300 | 15 | 3.3 | 3.50% |
| 30D | 33 | 35 | 40 | 1250 | 15 | 2 | 3.50% |
| 40D | 44 | 34 | 39 | 1230 | 20 | 2 | 3.50% |
| 50D | 55 | 34 | 39 | 1200 | 20 | 2.5 | 3.50% |
| 55D | 83 | 33 | 37 | 1200 | 30 | 2.5 | 3.50% |
| 100D | 111 | 33 | 37 | 1150 | 40 | 2.5 | 3.50% |
| 125D | 139 | 33 | 37 | 1100 | 50 | 2.5 | 3.50% |
| 150D | 165 | 32 | 36 | 1050 | 60 | 2.5 | 3.50% |
| 200D | 222 | 32 | 36 | 1050 | 80 | 2.5 | 3.50% |
| 250D | 275 | 32 | 36 | 1050 | 100 | 2.5 | 3.50% |
| 300D | 333 | 30 | 34 | 1000 | 120 | 2.5 | 3.50% |
| 350D | 389 | 30 | 34 | 1000 | 120 | 2.91 | 3.50% |
| 400D | 444 | 30 | 34 | 1000 | 160/240 | 2.50/1.66 | 3.50% |
| 500D | 555 | 30 | 34 | 1000 | 240 | 2.08 | 3.50% |
| 600D | 667 | 30 | 34 | 1000 | 240 | 2.08 | 3.50% |
| 800D | 889 | 28 | 32 | 900 | 320/480 | 2.50/1.66 | 3.50% |
| 1000D | 1111 | 28 | 32 | 900 | 360/480 | 2.77/2.08 | 3.50% |
| 1200D | 1333 | 28 | 32 | 900 | 480/720 | 2.50/1.66 | 3.50% |
| 1600D | 1778 | 28 | 32 | 900 | 640/960 | 2.50/1.66 | 3.50% |
| 2800D | 2999 | 28 | 30 | 900 | 960 | 2.5/1.66 | 3.50% |
Data Table
SPECIFICATION：20D
TENACITY(cN/dtex)：40
MODULUS（cN/dtex)（≥）：1300
MONOFILAMENT(denier)：3.3
ELONGATION AT BREAK: 3.5%
SPECIFICATION：30D
TENACITY(cN/dtex)：35
MODULUS（cN/dtex)（≥）：1250
MONOFILAMENT(denier)：2
ELONGATION AT BREAK: 3.5%
SPECIFICATION：40D
TENACITY(cN/dtex)：34
MODULUS（cN/dtex)（≥）：1230
MONOFILAMENT(denier)：2
ELONGATION AT BREAK: 3.5%
SPECIFICATION：50D
TENACITY(cN/dtex)：34
MODULUS（cN/dtex)（≥）：1200
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：55D
TENACITY(cN/dtex)：33
MODULUS（cN/dtex)（≥）：1200
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：100D
TENACITY(cN/dtex)：33
MODULUS（cN/dtex)（≥）：1150
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：125D
TENACITY(cN/dtex)：33
MODULUS（cN/dtex)（≥）：1100
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：150D
TENACITY(cN/dtex)：32
MODULUS（cN/dtex)（≥）：1050
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：200D
TENACITY(cN/dtex)：32
MODULUS（cN/dtex)（≥）：1050
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：250D
TENACITY(cN/dtex)：32
MODULUS（cN/dtex)（≥）：1050
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：300D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：1000
MONOFILAMENT(denier)：2.5
ELONGATION AT BREAK: 3.5%
SPECIFICATION：350D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：1000
MONOFILAMENT(denier)：2.91
ELONGATION AT BREAK: 3.5%
SPECIFICATION：400D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：1000
MONOFILAMENT(denier)：2.50/1.66
ELONGATION AT BREAK: 3.5%
SPECIFICATION：500D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：1000
MONOFILAMENT(denier)：2.08
ELONGATION AT BREAK: 3.5%
SPECIFICATION：600D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：1000
MONOFILAMENT(denier)：2.08
ELONGATION AT BREAK: 3.5%
SPECIFICATION：800D
TENACITY(cN/dtex)：28
MODULUS（cN/dtex)（≥）：900
MONOFILAMENT(denier)：2.50/1.66
ELONGATION AT BREAK: 3.5%
SPECIFICATION：1000D
TENACITY(cN/dtex)：28
MODULUS（cN/dtex)（≥）：900
MONOFILAMENT(denier)：2.77/2.08
ELONGATION AT BREAK: 3.5%
SPECIFICATION：1200D
TENACITY(cN/dtex)：28
MODULUS（cN/dtex)（≥）：900
MONOFILAMENT(denier)：2.50/1.66
ELONGATION AT BREAK: 3.5%
SPECIFICATION：1600D
TENACITY(cN/dtex)：28
MODULUS（cN/dtex)（≥）：900
MONOFILAMENT(denier)：2.50/1.66
ELONGATION AT BREAK: 3.5%
SPECIFICATION：2800D
TENACITY(cN/dtex)：30
MODULUS（cN/dtex)（≥）：900
MONOFILAMENT(denier)：2.50/1.66
ELONGATION AT BREAK: 3.5%